SF-1B Bronze Base Bearing for Heavy Machinery and Equipment

SF-1B bronze basic bearing is made of tin bronze as the base, sintered bronze spherical powder in the middle, and rolled PTFE and high temperature resistant filling materials on the surface. It has a high safety factor and is particularly suitable for places where continuous operation cannot be stopped for repairs and places where high temperature cannot be refueled. It has been widely used in the metallurgical steel industry, continuous casting machine billet raceways, high temperature furnace front equipment, cement grouting pumps and screw conveyors. It can be combined with steel sleeves on the outside, or it can be made into flanges to achieve the effect of simultaneous friction of the end face and the inner hole. The sliding part of the bridge support uses SF-1B wear-resistant layer thickened products to replace pure PTFE plates to meet the requirements of 130N/mm2 shaft load.

Ottieni un preventivo

PREV：SF-1D Hydraulic Special Bearing High-Performance for Hydraulic Systems NEXT：SF-1W Durable Self-Lubricating Lead-Free Bearing Corrosion-Resistant

introduzione al prodotto
Parametro
descrizione del materiale
Contattaci

caratteristiche del prodotto

1 Può funzionare a lungo in condizioni prive di olio.

2 Più adatto per condizioni di lavoro a bassa velocità e carichi pesanti, con buona resistenza all'usura e attrito estremamente basso.

3 Adatto per situazioni in cui è difficile che si formi un film d'olio, come ad esempio nei sistemi alternativi, rotanti e movimenti intermittenti.

4 Resistente alla corrosione e all'ossidazione.

5 Esente da manutenzione e lunga durata.

Perché scegliere i cuscinetti senza olio

Ridurre i costi di produzione

Non è necessario alcun dispositivo di alimentazione dell'olio, foro di iniezione dell'olio o olio lavorazione della scanalatura, che può ridurre notevolmente i costi di produzione.

Ridurre i costi operativi

Riduce notevolmente l'utilizzo di olio lubrificante, riduce la manutenzione delle apparecchiature, ed evita i pericoli nascosti causati da un'insufficiente fornitura di petrolio, riducendo efficacemente costi operativi.

Riduci i tempi di progettazione

Il design oil-free semplifica la struttura del prodotto e fa risparmiare efficacemente tempo di progettazione. Siamo professionali Fornitori ODM di SF-1B Bronze Base Bearing for Heavy Machinery and Equipment

Favorevole alla protezione dell'ambiente

Non è necessario il riciclaggio degli oli usati, il che è vantaggioso anche per la protezione dell'ambiente.

Campi di applicazione

Alta temperatura

·Fabbrica di acciaio

·Forno fusorio

·Attrezzature per l'asciugatura

·Forno

·Regolatore di calore

Impermeabile

·Porta della diga

·Pompa dell'acqua

·Struttura dell'interruttore del fluido

·Strutture offshore

·Attrezzature per banchine e macchine per il limo

Industria chimica

·Fabbrica chimica

·Attrezzature galvaniche

·Attrezzature per il trattamento delle acque reflue

·Macchine per tintura

·Attrezzature per la raffinazione del petrolio e dei prodotti chimici

Energia

·Energia eolica

·Nuova energia

Nave

·Gru a ponte

·Ancora

·Coperchio del portello

·Braccio del timone

·Macchine di sollevamento e attrezzature per anelli di sollevamento

Produzione automobilistica

·Stampo per stampaggio

·Struttura di saldatura

·Linea di verniciatura e asciugatura

·Nastro trasportatore in metallo

·Macchine utensili

Industria pesante

·Macchine per la produzione di tubi in acciaio

·Pneumatici e cartiere

·Centrale elettrica

·Novità di collegamento delle macchine per iniezione stampi

Edilizia, estrazione mineraria, caricamento

·Miscelatori, trituratori, polverizzatori

·Macchine da cantiere

·Attrezzature minerarie

·Cuscinetti di biella

Ponti e binari di sollevamento

·Appoggi del ponte

·Travi, ponti, ponti sospesi

·Reattori legati all'energia nucleare

·Generatore di vapore

Technical Parameters

●Maximum bearing pressure: 140N/mm2
●Applicable temperature range: -195~+300℃
●Maximum sliding speed: 5m/s
●Friction coefficient: 0.03~0.18
●Maximum allowable PV value (dry): 4.3N/mm2 .m/s
●Maximum allowable PV value (oil): 50N/mm2 .m/s

Metallographic Structure and Material Structure

①Polytetrafluoroethylene and lead mixture 0.01~0.03mm
②Spherical bronze powder 0.2~0.3mm
③Copper back 0.7~2.3mm

Application Features

●The mixture of PTFE and lead can form a good transfer film to protect the grinding shaft during movement.
●The sintered layer and the copper substrate have good thermal conductivity and can quickly transfer the heat generated during operation.
●Copper has self-lubricating properties and can be used in parts that cannot be shut down for maintenance due to long-term operation.
●The base copper has good corrosion resistance and can be used in weak acid and strong alkali situations.
●It has good load-bearing capacity.
●The product has been widely used in the metallurgical steel industry, high-temperature furnace steel ring parts, cement grouting pumps, screw conveyors, port machinery and ship machinery, etc.
●It can be combined with a steel sleeve on the outside; or made into a flange to achieve the effect of using the inner hole and the end face at the same time.

Chemical Properties

Model	Air	Vacuum	Water	Steam	Weak acid	Medium acid	Strong acid	Alkaline solution
SF-1B	good	good	good	good	medium	N/A	N/A	good

MMD-10 End Surface Friction and Wear Test

Model	Test Duration	Test Conditions			Friction Coefficient	Final Temperature	Final Wear Amount
Model	Test Duration	Lubrication Type	Speed	Pressure	Friction Coefficient	(℃)	(mm)
SF-1B	3hr	Dry	0.4m/s	3.5N/mm2	0.151	83	0.014
SF-1B	3hr	Oil	0.4m/s	3.5N/mm2	0.058	55	0.012

Composizione e proprietà dei materiali
Materiale	CuZn25Al5Mn3Fe3	CuSn5Pb5Zn5	CuAl10Ni5Fe5	CuSn12	CuZn25Al5Mn4Fe3
Densità	8.0	8.9	7.8	8.9	8.0
DurezzaHB	>210	>70	>150	>95	>250
Resistenza alla trazione N/mm²	>750	>200	>600	>260	>800
Carico di snervamento N/mm²	>450	>90	>260	>150	>450
Allungamento%	>12	>15	>10	>৪	>800
Coefficiente di dilatazione lineare 10 ^-5 /℃	1.9	1.8	1.6	1.8	1.9
Limite temperatura ℃	-40~300	-40~400	-40~400	-40~400	-40~150
Massimo. Carico N/mm²	100	60	50	70	120
Massimo. Velocità (a secco) m/min	15	10	20	10	15
Max.PV N/mm²*m/min	200	60	60	80	200
Compressione della deformazione permanente 300N/mm²	<0,01	<0,05	<0,04	<0,05	<0,05
*È disponibile una grande richiesta di materiali speciali.

Scambio di materiali di base
Codici materiali	Marchi cinesi GB1176-87	Internazionale ISO 1338	Germania DIN	Giappone JIS	America ASTM(ONU)	Inghilterra Che cavolo	Italia JM	Condizioni applicabili
Bronzo fuso JDB	ZCuZn25AI5 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 C86300	HTB2	JM18-1	Carico elevato, bassa velocità Comunemente utilizzato
JDB-1Bronzo	ZCuSn5 Pb5Zn5	GCuPb5 Sn5Zn5	DIN1705 G-CuSn5ZnPb	H5111 BC6	B30-92 C83600	LG2	JM7-15	Carico medio, bassa velocità Comunemente utilizzato
JDB-2Bronzo	ZCuAI9Fe4 Ni4Mn2	GCuAI10 FeNiS	DIN17656 G-CuAI10Ni	H5114 AIBC3	B30-92 C95500	AB2	JM3-15	Carico medio, velocità media, comunemente usato
JDB-3Bronzo	ZCuSn12		G-CuSn12	CAC503B	B30-92 C90800	PB2	JM1-15	Carico medio, bassa velocità, comunemente usato
JDB-5	ZCuZn25AI6 Fe3Mn3	GCuZn25AI6 Fe3Mn3	DIN1709 G-CuZn25AI5	H5102 CAC304	B30-92 C86300	HTB2	JM18-1	Utilizzo di carico elevato, bassa velocità, carico elevato

Lubrificante solido
Lubrificante	Caratteristiche	Applicazione tipica
SL1 Aggiunta di grafite	Eccellente resistenza agli agenti chimici attacchi e basso attrito, limite di temperatura 400 ℃	Vestito per macchine generali e sotto atmosfera
SL4 Aggiunta di PTFE	Basso attrito e buona lubrificazione con acqua, limite di temperatura 300 ℃	Nave, turbina idraulica, turbina a gas, ecc.

SUBMIT

Chi siamo

Zhejiang Mingxu Machinery Manufacturing Co., Ltd. precedentemente nota come Jiashan Mingxu Precision Machinery Factory, è stata fondata nel 2011. L'azienda è situata nell'entroterra della zona dimostrativa di sviluppo integrato del delta del fiume Yangtze, con posizione e comodi trasporti. Con oltre dieci anni di esperienza nella produzione e nella ricerca e sviluppo, l'azienda è stata profondamente coinvolta nello sviluppo e nella produzione di cuscinetti lubrificanti solidi, skateboard, guide di scorrimento e dispositivi di scorrimento. Fornitori e società ODM di cuscinetti autolubrificanti intarsiati in grafite con flangia a boccola spalla JFB in Cina. La produzione del prodotto adotta moderne apparecchiature di automazione, implementa rigorosamente lo standard del sistema di gestione della qualità ISO2000 e i processi principali vengono elaborati da macchine CNC ad alta precisione. I prodotti principali dell'azienda coprono una serie di prodotti come cuscinetti autolubrificanti integrati solidi JDB, cuscinetti sinterizzati in acciaio-rame, cuscinetti autolubrificanti SF-1, cuscinetti autolubrificanti perimetrali SF-2 e cuscinetti in rame FB090. Ampiamente utilizzato nell'industria automobilistica, nelle macchine edili, nelle attrezzature metallurgiche, nelle macchine minerarie, nello stampaggio a iniezione, negli stampi, nel tessile, nella stampa e in molti altri settori di produzione di macchinari; Fino ad ora, i prodotti dell'azienda si sono diffusi in tutta la Cina ed esportati in molti paesi stranieri e sono profondamente riconosciuti e amati dai clienti nazionali ed esteri. Mingxu Machinery aderisce al principio del servizio di "servizio di alta qualità orientato alla qualità" e si impegna a fornire ai clienti prodotti e servizi professionali. Fornitura all'ingrosso MXB-JFB Boccola spalla Flangia Cuscinetto autolubrificante intarsiato in grafite. L'azienda continuerà a introdurre talenti, a migliorare il meccanismo di gestione, l'integrità, lo sviluppo, l'innovazione e si impegnerà a costruire un marchio di livello mondiale.